Method and installation for laser welding with an ar/he gas mixture, the ar/he contents being controlled according to the laser power

ABSTRACT

The invention relates to a laser beam welding method and installation that makes use of a protective gas mixture containing argon and helium. The proportion of argon and/or helium in said gas mixture is chosen or adjusted according to the power or the power density of the laser beam. The laser power is included between 0.5 kW and 30 kW and, preferably, between 5 kW and 20 kW. The protective gas mixture comprises argon and/or helium and, preferably, the gas mixture contains a volume proportion of helium of between 30% and 80%, the remainder being argon and, possibly, inevitable impurities.

The present invention relates to a laser beam welding process using a gas mixture consisting of argon and helium in proportions that are adjusted or adapted according to the power or power density of the laser device used.

In industry, it is known to use a laser beam to cut or weld one or more metal workpieces. In this regard, the following documents may be cited: DE-A-2 713 904, DE-A-4 034 745, JP-A-01048692, JP-A-56122690, WO 97/34730, JP-A-01005692, DE-A-4 123 716, JP-A-02030389, US-A-4 871 897, JP-A-230389, JP-A-62104693, JP-A-15692, JP-A-15693, JP-A-15694, JP-A-220681, JP-A-220682, JP-A-220683, WO-A-88/01553, WO-A-98/14302, DE-A-3 619 513 and DE-A-3 934 920.

Laser welding is a very high-performance welding process as it makes it possible to obtain, at high speeds, very great penetration depths compared with other more conventional processes, such as plasma welding, MIG (Metal Inert Gas) welding or TIG (Tungsten Inert Gas) welding.

This is explained by the high power densities involved when focusing the laser beam by one or more mirrors or lenses in the joint plane of the workpieces to be welded, for example power densities that may exceed 10⁶ W/cm².

These high power densities cause considerable vaporization at the surface of the workpieces which, expanding to the outside, induces progressive cratering of the weld pool and results in the formation of a narrow and deep vapor capillary called a “keyhole” in the thickness of the plates, that is to say in the joint plane.

This capillary allows the energy of the laser beam to be directly deposited depthwise in the plate, as opposed to the more conventional welding processes in which the energy deposition is localized on the surface.

This capillary is formed from a metal vapor/metal vapor plasma mixture, the particular feature of which is that it absorbs the laser beam and therefore traps the energy within the actual capillary.

One of the problems with laser welding is the formation of a shielding gas plasma.

This is because this metal vapor plasma, by seeding the shielding gas with free electrons, may induce the appearance of a shielding gas plasma, which is prejudicial to the welding operation.

The incident laser beam may therefore be greatly, or even totally, absorbed and therefore may lead to a substantial reduction in the penetration depth, or even in a loss of coupling between the beam and the material and therefore a momentary interruption in the welding process.

The power density threshold at which the plasma appears depends on the ionization potential of the shielding gas used and is inversely proportional to the square of the wavelength of the laser beam.

Thus, it is very difficult to weld under pure argon with a CO₂-type laser, whereas this operation may be carried out with very much less of a problem with a YAG-type laser.

In general, in CO₂ laser welding, helium is used as shielding gas, this being a gas with a high ionization potential and making it possible to prevent the appearance of the shielding gas plasma, and to do so irrespective of the laser beam power employed.

However, helium has the drawback of being an expensive gas and many laser users prefer to use other gases or gas mixtures that are less expensive than helium but which would nevertheless limit the appearance of the shielding gas plasma and therefore obtain welding results similar to those obtained with helium, but at a lower cost.

Thus, gas mixtures are commercially available that contain argon and helium, for example the gas mixture containing 30% helium by volume and the rest being argon, sold under the name LASAL™ 2045 by L'Air Liquide™, which make it possible to achieve substantially the same results as helium, for CO₂ laser power levels below 5 kW and provided that the power densities generated are not too high, that is to say above about 2000 kW/cm².

However, the problem that arises with this type of Ar/He mixture is that it is no longer suitable for higher laser power densities, since the threshold at which the shielding gas plasma is created is then exceeded.

It is an object of the present invention therefore to solve this problem by proposing an improved laser welding process that can employ lasers with a power exceeding 15 to 20 kW and to do so, with no or minimal shielding gas plasma formation, irrespective of the power or power density chosen.

The solution of the invention is therefore a laser beam welding process employing a shielding gas mixture containing argon and helium, in which the proportion of argon and/or helium in said gas mixture is chosen or adjusted according to the power or power density of said laser beam.

Depending on the case, the process of the invention may include one or more of the following technical features:

-   -   the laser power is between 0.5 kW and 30 kW, preferably between         5 kW and 20 kW;     -   the shielding gas mixture consists of argon and/or helium;         preferably, the gas mixture contains a helium volume proportion         of 30% to 80%, the remainder being argon and possibly inevitable         impurities;     -   the gas mixture is produced on site, by mixing defined amounts         of argon and helium;     -   the gas mixture is produced by means of a gas mixer system         slaved to the laser power or power density employed so as to mix         controlled amounts of argon and helium;     -   the proportion of helium in the gas mixture is increased when         the laser power or power density is increased.

According to another aspect, the invention also relates to a laser beam welding process employing a shielding gas mixture containing helium and argon, in which the proportion of helium relative to the proportion of argon in said gas mixture is chosen or adjusted according to the power or power density of said laser beam so as to avoid or minimize plasma formation in the shielding gas during welding.

According to another aspect, the invention also relates to a laser beam welding process employing a shielding gas mixture containing helium and argon, in which the volume proportion of helium in said gas mixture is:

-   -   between 1 and 30% for a laser beam power of between 0.5 kW and 4         kW;     -   between 30 and 50% for a laser beam power of between 4 kW and 8         kW; and/or     -   between 50 and 70% for a laser beam power of between 8 kW and 12         kW.

Moreover, the invention also relates to a laser beam welding process employing a shielding gas mixture containing helium and argon, in which the volume proportion of helium in said gas mixture is:

-   -   between 1 and 30% for a laser beam power density of between 500         kW/cm² and 2000 kW/cm²;     -   between 30 and 50% for a laser beam power density of between         2000 kW/cm² and 4000 kW/cm²; and/or     -   between 50 and 70% for a laser beam power density of between         4000 kW/cm² and 10,000 kW/cm².

The helium and argon come from a single gas source in which the helium and argon are premixed in the desired proportions, for example by means of a gas mixer.

The invention also relates to a laser beam welding installation employing a shielding gas mixture containing argon and helium, comprising:

-   -   at least one argon source;     -   at least one helium source;     -   gas mixing means allowing the argon coming from the argon source         to be mixed with the helium coming from the helium source;     -   a laser generator device delivering a laser beam having a laser         power of at least 0.5 kw; and     -   regulating means that cooperate with said gas mixing means so as         to adjust the proportions of argon and/or helium according to         the laser power delivered by the laser device.

Furthermore, the invention also relates to a laser beam welding process employing a shielding gas mixture containing helium and argon, in which the volume proportion of helium (%He) in said gas mixture as a function of the power density is such that:

-   -   28×In(Φ_(p))−207≦%He≦32.3×In(Φ_(p))−207 in which:     -   In(Φ_(p)) represents the natural logarithm of the power density         expressed in kW/cm²; and     -   %He represents the volume percentage of helium in argon of the         gas mixture.

Preferably, the volume proportion of helium (%He) in said gas mixture as a function of the power density is such that:

-   -   28.5×In(Φ_(p))−207≦%He≦31.5×In(Φ_(p))−207.

Also preferably, the volume proportion of helium (%He) in said gas mixture as a function of the power density is such that:

-   -   29×In(Φ_(p))−207≦%He≦31×In(Φ_(p))−207.

A greater understanding of the invention will now be gained from the explanations given below with reference to the appended figure.

As explained above, in laser beam welding, a major problem that arises is associated with the creation of a shielding gas plasma harmful to the welding operation by the strong, or even total, absorption of the laser beam that it generates, and thus results in an appreciable reduction in the penetration depth, or even in a loss of coupling between the laser beam and the material to be welded, and therefore in an interruption in the welding process.

Now, the inventors of the present invention have demonstrated that the threshold for the appearance of the shielding gas plasma is determined, for a given CO₂-type laser power density, by the volume proportion of helium (relative to that of argon) in the helium/argon gas mixture used as shielding gas during the welding operation and that this proportion of helium has to be varied according to the power density of the laser.

Thus, FIG. 1 shows (curve A) the change in the threshold appearance of plasma as a function of the power density (plotted on the x-axis) and of the volume proportion of helium (plotted on the y-axis) in the mixture formed from argon and helium, the sum of the argon and helium contents constituting 100% by volume of the mixture.

Curve A was obtained by analysis of the depth of penetration of the weld beads produced with various helium contents in the mixture and by visual examination of the appearance, or nonappearance, of the shielding gas plasma during the welding process.

The power density was obtained by dividing the laser power on the workpiece by the diameter of the focal spot obtained with the laser in question, measured beforehand by means of a laser beam analyzer.

The region lying above curve A represents the region in which, for the power density in question, the helium content in the argon allows a weld bead to be produced without shielding gas plasma appearing.

In the region lying below curve A, the shielding gas breaks down and therefore a shielding gas plasma is present.

In order to indicate the uncertainties associated with measuring the diameter (in microns) of the focal spot, with that of the helium content in the argon/helium mixture and with that regarding the energy distribution within the focal spot, three bundles of curves (B, C), (D, E) and (F, G) have also been shown in FIG. 1.

The equations of these curves are of the type: %He=μ×In(Φ_(p))−207 in which:

-   -   In(Φ_(p)) represents the natural logarithm of the power density         expressed in kW/cm²;     -   %He is the helium percentage in the argon; and     -   μ is a value that depends on the curve in question: μ=31 for         curve B; μ=29 for curve C; μ=31.5 for curve D; μ=28.5 for curve         E; μ=32.3 for curve F; and μ=28 for curve G.

Thus, within the area of the drawing lying between curves F and G (or alternatively D and E or B and C), it is possible to choose, for the power density in question, the Ar/He mixture that makes it possible to obtain the same performance as either pure helium or as an Ar/He mixture located above the region lying between curves F and G (or alternatively D and E or B and C).

Conversely, below this region the shielding gas always breaks down and therefore a shielding gas plasma appears. The gas mixture determined from these curves is therefore the optimum mixture, that is to say the one which contains the least helium but which gives, however, substantially the same results as pure helium or as a mixture with a higher proportion of helium.

All these curves were produced at a welding speed of 3 m/min on steel and stainless steel workpieces with a parabolic mirror of 250 mm, 200 mm or 150 mm focal length, and using a CO₂ laser whose Q-factor was 4.

As shown in FIG. 1, a helium/argon mixture containing 50% by volume of argon gives penetration depths and welding speeds that are approximately the same as for pure helium for a CO₂ laser power density of 5.3×106 W/cm².

The invention may also be demonstrated by showing the change in the threshold for the shielding gas plasma to appear as a function of the helium content in argon and of the laser power employed, as shown diagrammatically in FIG. 2.

This other representation, less general than the previous one, may be obtained from the curves of FIG. 1 and using the following equations: Φ_(p) =P/S  (1) where Φ_(p) is the power density, P is the laser power used and S is the area of the focal spot; S=πW ₀ ²  (2) where W₀ is the radius of the focal spot; and W ₀ W _(F) =M ²(λf/π)  (3) where W_(F) is the radius of the laser beam at the mirror or at the focusing lens for the power in question, M² is the Q-factor of the laser beam, which in general is a manufacturer's datum (M²=1 for a Gaussian beam), λ is the wavelength of the laser beam (10.6 μm in the case of a CO₂ laser) and f is the focal length of the mirror or of the focusing lens.

Thus, it is possible to switch from a power density representation (FIG. 1) to a power representation (FIG. 2), and vice versa, using the above equations, in order to determine on the basis of the power or power density used the corresponding argon/helium mixture.

FIG. 2 was obtained in this case from the curves of FIG. 1, and for a Q-factor of 4, a focal length of 200 mm and a beam diameter at the focusing mirror of 28 mm.

Thus, at 6 kW, with a focal length of 200 mm, for a laser of 4 Q-factor and a beam diameter at the focusing mirror of 200 mm, it is possible to use an argon/helium mixture containing 50% by volume of each of these components.

The present invention is therefore based on the fact that the Ar/He gas mixture is adapted or adjusted according to the laser power or power density used in order to obtain a high-quality weld and for reduced cost, without shielding gas plasma generation or else with as little plasma generation as possible.

According to the invention, the proportions of the components in the gas mixture may be adjusted on the basis of the volume, molar or mass proportions; however, a volume adjustment is preferred as it is simpler to implement.

Starting from this basis, the invention may be implemented by producing a range of gas mixtures in bottles, that is to say in packaged form, with a variable helium content in the argon adapted according to the laser power or power density.

For example, the table below gives three different Ar/He mixtures adapted to three respective ranges of laser power density recommended for implementing the invention. Composition of the Ar/He gas mixture (expressed as Recommended laser power vol % of He) density ranges Ar + 30% He 500 to 2000 kW/cm²  Ar + 50% He 2000 to 4000 kW/cm²  Ar + 70% He 4000 to 10000 kW/cm²

Depending on the case, the invention may also be used directly on site by an operator, before the start of welding, for example on the basis of a source of helium and argon, the Ar/He gas mixture most suited to the power density or to the power of the laser used, and according to the specifications of the figure appended hereto.

Alternatively, the desired Ar/He mixture may also be obtained by automatic slaving of a gas mixer according to the power or power density of the laser used and by using the curve of the figure appended hereto as calibration curve.

The laser welding process of the invention is particularly suitable for welding workpieces made of aluminum or aluminum alloys, stainless steel or mild steel.

The laser welding process of the invention may be used for welding workpieces of the same or different thickness ranges between 0.1 mm and 300 mm. 

1-14 (canceled)
 15. A laser beam welding method comprising employing a shielding gas mixture comprising argon and helium, in which the proportion of one or more of said argon or said helium in said gas mixture is chosen according to one or more of the laser power or the power density of said laser beam.
 16. The method of claim 15, wherein said laser power is between 0.5 kW and 30 kW.
 17. The method of claim 16, wherein said laser power is between 5 kW and 20 kW.
 18. The method of claim 15, wherein said shielding gas mixture consists of a helium volume proportion of between about 1% and 70%, and the remainder consisting of one or more of argon or impurities.
 19. The method of claim 15, wherein said shielding gas mixture consists of a helium volume proportion of between about 30% and 80%, and the remainder consisting of one or more of argon or impurities.
 20. The method of claim 15, wherein said gas mixture is produced on site, by mixing defined amounts of argon and helium.
 21. The method of claim 20, wherein said gas mixture is produced by means of a gas mixer, and the proportion of said argon or said helium is controlled by one or more of said laser power or said power density.
 22. The method of claim 21, wherein said proportion of helium in said gas mixture is increased when one or more of said laser power or said power density is increased.
 23. A laser beam welding method comprising employing a shielding gas mixture comprising helium and argon, in which the proportion of said helium relative to the proportion of said argon in said gas mixture is chosen according to one or more of the laser power or power density of said laser beam, and wherein plasma formation in the shielding gas during welding is minimized.
 24. A laser beam welding method comprising employing a shielding gas mixture comprising helium and argon, in which the volume proportion of said helium in said gas mixture is: between 1 and 30% when 0.5 kW≦laser power≦4 kW; between 30 and 50% when 4 kW<laser power≦8 kW; or between 50 and 70% when 8 kW<laser power≦12 kW.
 25. A laser beam welding method comprising employing a shielding gas mixture containing helium and argon, in which the volume proportion of said helium in said gas mixture is: between 1 and 30% when 500 kW/cm²≦power density≦2,000 kW/cm²; between 30 and 50% when 2,000 kW/cm²<power density≦4,000 kW/cm²; or between 50 and 70% when 4,000 kW/cm²<power density≦10,000 kW/cm².
 26. The method of claim 15, wherein said helium and said argon come from a single gas source in which said helium and said argon are premixed in the desired proportions.
 27. A laser beam welding apparatus employing a shielding gas mixture containing argon and helium, comprising: (a) at least one argon source, (b) at least one helium source, (c) gas mixing means allowing the argon coming from said argon source to be mixed with the helium coming from said helium source, (d) a laser generator device delivering a laser beam having a laser power of at least 0.5 kW, and (e) a regulating means that controls said gas mixing means, wherein the proportion of said argon and said helium adjusted according to said laser power density.
 28. A laser beam welding method comprising employing a shielding gas mixture containing helium and argon, in which the volume proportion of helium is: 28×In(Φ_(p))−207≦%He≦32.3×In(Φ_(p))−207 wherein: In(Φ_(p)) represents the natural logarithm of the power density expressed in kW/cm², and %He represents said volume percentage of helium in said shielding gas mixture.
 29. The method of claim 28, wherein said volume proportion of helium is: 28.5×In(Φ_(p))−207≦%He≦31.5×In(Φ_(p))−207.
 30. The method of claim 29, wherein said volume proportion of helium is: 29×In(Φ_(p))−207≦%He≦31×In(Φ_(p))−207. 